Unshaped Silica Refractories Mortar For Hot Blast Stove
| 1.Grain- size Composition (%): | 1 |
| 2. Chemical Composition (%): | 94.0 |
| 3. Refractoriness Under Load (0.2MPa) ≥: | 1600 |
| 4. Bonding Time (min): | 1~2 |
E-mail:sinorefr@163.com
Description
Silica refractories mortar for hot blast stove is a traditional refractory material. Refractory mortar is usually used to build and bond the refractory bricks, and also used to repair of furnace lining in hot blast furnace. Silica refractories mortar is an important part of refractory mortar which is as Cab-O-sil or adding some ganister sand as main raw materials, the binder adopts mild-clay or chemical bond. Our Silica refractories mortar for the hot stoves can meet all the above stated requirements.
Main features of Silica refractory mortar:
1. High adhesive strength.
2. High refractoriness.
3. Excellent refractoriness under load.
4. Good installation performance.
Main features of Silica refractory mortar:
1. High adhesive strength.
2. High refractoriness.
3. Excellent refractoriness under load.
4. Good installation performance.
Specification
| Unshaped Silica Refractories Mortar For Hot Blast Stove | RT-RGN-94 | |||
| Refractoriness,Cone No. | 170 | |||
| Cold Rupture Bonding Strength (MPa) | (Drying at 110℃) | 1.0 | ||
| (Firing at 1400℃x3h) | 3.0 | |||
| Bonding Time (min) | 1~2 | |||
| Grain- size Composition (%) | +0.5mm ≤ | 1 | ||
| -0.074mm ≥ | 60 | |||
| Chemical Composition (%) | SiO2 ≥ | 94.0 | ||
| Fe2O3 ≤ | 1.0 | |||
| Refractoriness Under Load (0.2MPa) ≥ | 1600 | |||